Top: PL.8622B-5000(6); Primer: PL.8622A(2）
Product | Double layer water-soluble polyether sulfonic fluorine nonstick coating |
Model | Top : PL.8622B-5000（6） Primer : PL.8622A(2) |
Color | Black |
Main Chemical Composition | PES Binder, PTFE Anti-adherent, Pigment filler, Mixed Aqueous Solution |
Viscosity (Room Temperature of 25℃, IWATA NK-2 Viscosity Cup) | Top Coat: 16 to 30s Primer Coat: 23 to 40s (Due to the influence of climate and temperature, a moderate deviation is normal.) |
Specific Weight | 0.98-1.06KG/L |
Solid-containing Content | Top : 34%±2% Primer : 30%±2% |
Sintering Temperature | Top : 385-425℃ Primer : 130-180℃ |
Coating Thickness | 22 to 32um |
Packaging Specification | 20kg per plastic barrel with carton |
Storage Condition | Avoid high temperature exposure. Should be stored in a ventilated and cool environment at room temperature. |
Shelf Life | 6 Months |
Application | All kinds of kitchenware and tableware made from metal, aluminum, stainless steel, etc. |
Property Testing | Standard | Method |
Appearance of Original Paint | Thick and Sticky Liquid | Eyeballing |
Appearance of Coating Film | Flat and smooth without obvious,roughness,bittiness,discoloration,and scratches. | Eyeballing |
Adhesion | No fall-off of the coating film | 50-KG recoil for 2 times. Scrape the coating surface with a knife on the breach. Then scrape it down with nails, and there should be no obvious peeling off. |
Layer Adhesion | The falling grid should be 1 or less when 3M tape is pulled 5 times in different directions. | Draw a 100-square grid of 1mm X 1mm on the surface of the coating, then drag a 3M tape to test. |
Hardness | ≥2H | Use 2H pencil with hardness tester for the coating. |
Acid Resistance | No abnormality of the coating film | Boil for 20 minutes in a reagent hydrochloric acid solution with a volume fraction of 12% |
Boiling Water Resistance | No fall-off of the coating film | Test the adhesion after boiling water for 100 hours |
Corrosion Resistance | No fall-off of the coating film | Boil for 100 hours in the salt water with a volume fraction of 5%, heating to the temperature of over 90℃ |
Anti-stick | Good | Boil milk and fry egg without stick |
Heat Resistance | No fall-off of the coating film | Put the sample into the oven of 260℃ for 10 hours. Wait for it to cool down to room temperature and take it out for Observation.
|
Abrasion Resistance (Test item is the inner container of a rice cooker with the R base) | After 200-time abrasion or more, there is no obvious wear-out on the coating. Abrasion marks that are less than 1mm should be 2 or less.
| Wet grinding test with coating wear-resistant instrument (5% dishwashing liquid +95% tap water), with 3M 7447B cloth and 3KG weight pressure, back and forth for once, 500 times turn one side.
|
Abrasion Resistance (Test item is flat aluminium alloy plate) | After 500-time abrasion or more, there is no obvious wear-out on the coating. Abrasion marks that are less than 1mm should be 2 or less. | Wet grinding test with coating wear-resistant instrument (5% dishwashing liquid +95% tap water), with 3M 7447B cloth and 3KG weight pressure, back and forth for once, 500 times turn one side. |
Health Indicator | International Standard | Certification of ROHS, FDA, LFGB, REACH |
Test Standard | National Standard | GB/T32095.1-2015 GB/T32095.2-2015 GB/T32095.3-2015 GB/T32095.4-2015 |
Applications of PES Non-stick Coating
·Easy-cleaning
·Long Service Life
·Super Heat-resistant
·Environmental & Safe
·Strong Adhesion
·Great Rigidity
·High Practicability & Processability
·Strong Chemical Resistance
Product | Double layer water-soluble polyether sulfonic fluorine nonstick coating |
Model | Top : PL.8622B-5000（6） Primer : PL.8622A(2) |
Color | Black |
Main Chemical Composition | PES Binder, PTFE Anti-adherent, Pigment filler, Mixed Aqueous Solution |
Viscosity (Room Temperature of 25℃, IWATA NK-2 Viscosity Cup) | Top Coat: 16 to 30s Primer Coat: 23 to 40s (Due to the influence of climate and temperature, a moderate deviation is normal.) |
Specific Weight | 0.98-1.06KG/L |
Solid-containing Content | Top : 34%±2% Primer : 30%±2% |
Sintering Temperature | Top : 385-425℃ Primer : 130-180℃ |
Coating Thickness | 22 to 32um |
Packaging Specification | 20kg per plastic barrel with carton |
Storage Condition | Avoid high temperature exposure. Should be stored in a ventilated and cool environment at room temperature. |
Shelf Life | 6 Months |
Application | All kinds of kitchenware and tableware made from metal, aluminum, stainless steel, etc. |
Property Testing | Standard | Method |
Appearance of Original Paint | Thick and Sticky Liquid | Eyeballing |
Appearance of Coating Film | Flat and smooth without obvious,roughness,bittiness,discoloration,and scratches. | Eyeballing |
Adhesion | No fall-off of the coating film | 50-KG recoil for 2 times. Scrape the coating surface with a knife on the breach. Then scrape it down with nails, and there should be no obvious peeling off. |
Layer Adhesion | The falling grid should be 1 or less when 3M tape is pulled 5 times in different directions. | Draw a 100-square grid of 1mm X 1mm on the surface of the coating, then drag a 3M tape to test. |
Hardness | ≥2H | Use 2H pencil with hardness tester for the coating. |
Acid Resistance | No abnormality of the coating film | Boil for 20 minutes in a reagent hydrochloric acid solution with a volume fraction of 12% |
Boiling Water Resistance | No fall-off of the coating film | Test the adhesion after boiling water for 100 hours |
Corrosion Resistance | No fall-off of the coating film | Boil for 100 hours in the salt water with a volume fraction of 5%, heating to the temperature of over 90℃ |
Anti-stick | Good | Boil milk and fry egg without stick |
Heat Resistance | No fall-off of the coating film | Put the sample into the oven of 260℃ for 10 hours. Wait for it to cool down to room temperature and take it out for Observation.
|
Abrasion Resistance (Test item is the inner container of a rice cooker with the R base) | After 200-time abrasion or more, there is no obvious wear-out on the coating. Abrasion marks that are less than 1mm should be 2 or less.
| Wet grinding test with coating wear-resistant instrument (5% dishwashing liquid +95% tap water), with 3M 7447B cloth and 3KG weight pressure, back and forth for once, 500 times turn one side.
|
Abrasion Resistance (Test item is flat aluminium alloy plate) | After 500-time abrasion or more, there is no obvious wear-out on the coating. Abrasion marks that are less than 1mm should be 2 or less. | Wet grinding test with coating wear-resistant instrument (5% dishwashing liquid +95% tap water), with 3M 7447B cloth and 3KG weight pressure, back and forth for once, 500 times turn one side. |
Health Indicator | International Standard | Certification of ROHS, FDA, LFGB, REACH |
Test Standard | National Standard | GB/T32095.1-2015 GB/T32095.2-2015 GB/T32095.3-2015 GB/T32095.4-2015 |
Applications of PES Non-stick Coating
·Easy-cleaning
·Long Service Life
·Super Heat-resistant
·Environmental & Safe
·Strong Adhesion
·Great Rigidity
·High Practicability & Processability
·Strong Chemical Resistance