Product | Solvent polyether sulfonic fluorine nonstick coating |
Model | JH.O-2501-32 |
Color | Gold |
Main Chemical Composition | PES Binder, PTFE Anti-adherent, Pigment filler, Mixed Aqueous Solution |
Viscosity (Room Temperature of 25℃, IWATA NK-2 Viscosity Cup) | 18 to 60 Seconds (Due to the influence of climate and temperature, a moderate deviation is normal.) |
Specific Weight | 0.98-1.06KG/L |
Solid-containing Content | 23%±3% |
Sintering Temperature | 385-420℃ |
Coating Thickness | 18-22um |
Packaging Specification | 20kg per plastic barrel with carton |
Storage Condition | Avoid high temperature exposure. Should be stored in a ventilated and cool environment at room temperature. |
Shelf Life | 6 Months |
Application | All kinds of kitchenware and tableware made from metal, aluminum, stainless steel, etc. |
Property Testing | Standard | Test Method |
Appearance of Original Coating | Thick and Sticky Liquid | Eyeballing |
Appearance of Coating Film | Flat and smooth without obvious,roughness,bittiness,discoloration,and scratches. | Eyeballing |
Adhesion | The falling grid should be 1 or less when 3M tape is pulled 5 times in different directions. | Draw a 100-square grid of 1mm X 1mm on the surface of the coating, then drag a 3M tape to test. |
Hardness | No exposed base | Use 2H pencil with hardness tester for the coating. |
Acid Resistance | No abnormality of the coating film | Boil for 15 minutes in a reagent hydrochloric acid solution with a volume fraction of 12% |
Boiling Water Resistance | No fall-off of the coating film | Add pure water to the inner tank until the maximum mark water level. Put the inner tank into the electric pressure cooker and work continuously for 8 hours. Then work for 16 hours under the heat preservation state, which is 1 cycle and 4 cycles. During the test, be careful not to boil the water dry, and wash the inner tank with water after each cycle of the experiment. Observe the condition of the inner tank. |
Corrosion Resistance | No fall-off of the coating film | Add 5% salt water in the inner tank to the maximum scale water level. Put the inner tank in the electric pressure cooker and work continuously for 8 hours.Then work for 16 hours under the heat preservation state, which is 1 cycle and 4 cycles. During the test, be careful not to boil the water dry, wash the inner tank with water after each cycle of the experiment.Observe the condition of the inner tank. |
Test of Cooking Rice | Good | Put 3 cups of rice and 3 cups of water into a rice cooker of 3 to 4L. Keep it warm for 10 minutes after power-on cooking. Rice can be poured more than 2/3 at a time. (As different rice cookers have different effects, the test results are for reference only.) |
Thermal Test | The coating has no blister and fall-off | Heat the aluminum sample to the temperature of 250℃±5℃ with a constant temperature oven. Keep the sample warm for 5 minutes then immediately put it into the room-temperature water for cooling down for 1 minute. Later take it out of the water and dry it. Repeat the steps above for 5 times. |
Abrasion Resistance (Internal control of other color series) (Test item is a rice cooker with the R base) | After 500-time abrasion or more, there is no obvious wear-out on the coating. Abrasion marks that are less than 1mm should be 2 or less.
| Use abrasion tester for dry abrasion test, with scouring pad of 3M 7447B and 1.5-kg weight. Rubbing back and forth counts one time. |
Abrasion Resistance (Internal control of the internal coating of oil A, B) (Test item is a rice cooker with the R base)
| After 750-time abrasion or more, there is no obvious wear-out on the coating. Abrasion marks that are less than 1mm should be 2 or less. | Use abrasion tester for wet abrasion test. Apply 5% dishwashing liquid and 95% wate, use scouring pad of 3M 7447B and 3-kg weight to rub back and forth once. Turn over the surface every 500 times. |
Theoretical Coating Area | 7-11㎡/kg | Coating thickness should be 18 to 22um |
Health Indicator | International Standard | Certification of ROHS, FDA, LFGB, REACH |
Test Standard | National Standard | GB/T32095.1-2015 GB/T32095.2-2015 GB/T32095.3-2015 GB/T32095.4-2015 |
Applications of PES Non-stick Coating
·Easy-cleaning
·Long Service Life
·Super Heat-resistant
·Environmental & Safe
·Strong Adhesion
·Great Rigidity
·High Practicability & Processability
·Strong Chemical Resistance
Product | Solvent polyether sulfonic fluorine nonstick coating |
Model | JH.O-2501-32 |
Color | Gold |
Main Chemical Composition | PES Binder, PTFE Anti-adherent, Pigment filler, Mixed Aqueous Solution |
Viscosity (Room Temperature of 25℃, IWATA NK-2 Viscosity Cup) | 18 to 60 Seconds (Due to the influence of climate and temperature, a moderate deviation is normal.) |
Specific Weight | 0.98-1.06KG/L |
Solid-containing Content | 23%±3% |
Sintering Temperature | 385-420℃ |
Coating Thickness | 18-22um |
Packaging Specification | 20kg per plastic barrel with carton |
Storage Condition | Avoid high temperature exposure. Should be stored in a ventilated and cool environment at room temperature. |
Shelf Life | 6 Months |
Application | All kinds of kitchenware and tableware made from metal, aluminum, stainless steel, etc. |
Property Testing | Standard | Test Method |
Appearance of Original Coating | Thick and Sticky Liquid | Eyeballing |
Appearance of Coating Film | Flat and smooth without obvious,roughness,bittiness,discoloration,and scratches. | Eyeballing |
Adhesion | The falling grid should be 1 or less when 3M tape is pulled 5 times in different directions. | Draw a 100-square grid of 1mm X 1mm on the surface of the coating, then drag a 3M tape to test. |
Hardness | No exposed base | Use 2H pencil with hardness tester for the coating. |
Acid Resistance | No abnormality of the coating film | Boil for 15 minutes in a reagent hydrochloric acid solution with a volume fraction of 12% |
Boiling Water Resistance | No fall-off of the coating film | Add pure water to the inner tank until the maximum mark water level. Put the inner tank into the electric pressure cooker and work continuously for 8 hours. Then work for 16 hours under the heat preservation state, which is 1 cycle and 4 cycles. During the test, be careful not to boil the water dry, and wash the inner tank with water after each cycle of the experiment. Observe the condition of the inner tank. |
Corrosion Resistance | No fall-off of the coating film | Add 5% salt water in the inner tank to the maximum scale water level. Put the inner tank in the electric pressure cooker and work continuously for 8 hours.Then work for 16 hours under the heat preservation state, which is 1 cycle and 4 cycles. During the test, be careful not to boil the water dry, wash the inner tank with water after each cycle of the experiment.Observe the condition of the inner tank. |
Test of Cooking Rice | Good | Put 3 cups of rice and 3 cups of water into a rice cooker of 3 to 4L. Keep it warm for 10 minutes after power-on cooking. Rice can be poured more than 2/3 at a time. (As different rice cookers have different effects, the test results are for reference only.) |
Thermal Test | The coating has no blister and fall-off | Heat the aluminum sample to the temperature of 250℃±5℃ with a constant temperature oven. Keep the sample warm for 5 minutes then immediately put it into the room-temperature water for cooling down for 1 minute. Later take it out of the water and dry it. Repeat the steps above for 5 times. |
Abrasion Resistance (Internal control of other color series) (Test item is a rice cooker with the R base) | After 500-time abrasion or more, there is no obvious wear-out on the coating. Abrasion marks that are less than 1mm should be 2 or less.
| Use abrasion tester for dry abrasion test, with scouring pad of 3M 7447B and 1.5-kg weight. Rubbing back and forth counts one time. |
Abrasion Resistance (Internal control of the internal coating of oil A, B) (Test item is a rice cooker with the R base)
| After 750-time abrasion or more, there is no obvious wear-out on the coating. Abrasion marks that are less than 1mm should be 2 or less. | Use abrasion tester for wet abrasion test. Apply 5% dishwashing liquid and 95% wate, use scouring pad of 3M 7447B and 3-kg weight to rub back and forth once. Turn over the surface every 500 times. |
Theoretical Coating Area | 7-11㎡/kg | Coating thickness should be 18 to 22um |
Health Indicator | International Standard | Certification of ROHS, FDA, LFGB, REACH |
Test Standard | National Standard | GB/T32095.1-2015 GB/T32095.2-2015 GB/T32095.3-2015 GB/T32095.4-2015 |
Applications of PES Non-stick Coating
·Easy-cleaning
·Long Service Life
·Super Heat-resistant
·Environmental & Safe
·Strong Adhesion
·Great Rigidity
·High Practicability & Processability
·Strong Chemical Resistance